|Properties andTest Methods||Units||ACEMATT TS 100|
|Loss on drying2 h at 105°C
following ISO 787-2
|Loss on ignition 1)2 h at 1000°C
following ISO 3262-1
|pH value5% in water
following ISO 787-9
|Sulfate content as SO4IR spectrometrically
|Particle sizeMean (TEM)
d50 value (Laser diffraction)
|Tamped densitynot sieved
following ISO 787-11
|Densityfollowing ISO 787-10||g/cm3||1.9|
|Oil absorptionfollowing ISO 787-5||g/100g||220|
|SiO2 content 2)following ISO 3262-19||%||98|
|TSCA (USA), AICS (Australia) PICCS (Philippines)
ACEMATT HK 125
An economical, untreated all-purpose matting agent; hetero- geneous particle distribution;
particle size 1): 4µm; for pigmented coatings, in particular coil coating systems, wood and industrial paints.
ACEMATT HK 400
An all-purpose untreated matting agent in the particle size 1) range of 3µm.
ACEMATT HK 450
Untreated matting agent produced by a newly developed pro- duction process.
This high efficiency matting agent is designed for low gloss : sheen coatings e.g. coil-coatings. Particle size 1): 3µm.
ACEMATT HK 460
Untreated matting agent. High matting efficiency combined with excellent smooth coating surface;
universal to different coating applications; particle size 1): 2.5µm.
ACEMATT OK 412
Easily dispersible all-purpose matting agents; wax treated;
par- ticle size 1): 3µm. Outstanding suspension characteristics.
ACEMATT OK 500 is recommended for coatings in which ACEMATT OK 412 may cause drying retardation.
ACEMATT OK 412 LC
Easily dispersible matting agent with low conductivity;
wax treat- ed;
particle size 1): 3µm.
In view of its very low conductivity ACEMATT OK 412 LC is ideal
for use as a functional filler and matting agent in electronic deposit coatings.
ACEMATT OK 520
Easily dispersible, all-purpose matting agent;
particle size 1): 3µm. ACEMATT OK 520 is especially recommended for clear coats e.g.
PU-systems because of the high matting efficiency and transparency.
ACEMATT OK 607
Easily dispersible matting agent with extremely fine particles 1) in the range of 2µm;
A very high degree of surface smoothness, good transparency and outstanding sheen which result from the fineness of the particles.
This product is ideal for thin layer coatings and water based paint systems.
ACEMATT TS 100
A thermal silica without surface treatment obtained by the Aerosil process;
particle size 1): 4µm. ACEMATT TS 100 has superior matting efficiency and transparency and is suitable for all coatings especially for water-bas
ACEMATT® OP 278
Organic matting agent. Suitable for matting plastic semi-pro- ducts such as films, cables, boards and non-pressurized pipes.
Average agglomerate particle size, determined by means of transmission-electron microscopy images (TEM)